Martensitic microstructure with good resistance to abrasion, impact and compression. Applicable for cladding parts of steels, cast steels and high Mn-steel, subjected a simultaneously to abrasion, impact and compression. Typical application fields are the earth moving and stone treatment industry, e.g. excavator bucket teeth, crusher jaws and cones, mill hammers, rotors, etc. Good weldability and easy slag removal, machining of the weld metal possible by grinding only. |
Description
Material Type Alloy Components
High Iron , Chromium (Fe – Cr)
Weld Deposit Characteristics
Martensitic microstructure with good resistance to abrasion, impact and compression. Good weldability and easy slag removal, machining of the weld metal possible by grinding only.
Weld Deposit Properties
Recommended Application
Suitable for Applicable for cladding parts of steels, cast steels and high Mn-steel, subjected a simultaneously to abrasion, impact and compression. Typical application fields are the earth moving and stone treatment industry, e.g., excavator bucket teeth, crusher jaws and cones, mill hammers, rotors, etc.
Standard Sizes
Diameter: 2.5/3.25/4.0/5.0 mm
Packing : 5.0 Kg Packages – 2.0 Kg Vacuum Package
Operating Data
Welding Positions
- All Positions Except Vertical Down
Polarity
- AC & DC (+)
Notes on usage:
Preheating recommended for heavy parts and higher tensile steels to 200 – 300°C. On high Mn-Steel, cold welding (interpass temperature max. 250°C) is recommended. If necessary, intermediate cooling.
We do hereby certify that; the weld metal deposit, has been tested, mechanically and chemically and all results are comply with the requirements of specifications of Elkadesia for engineering industries and the Specification of ASME II part C SFA 5.01 Class C5 and level of tests in J or 5.