Weld Metal Deposit Analysis
|
C | Si | P | S | Cr | Fe |
| Wt. % |
2.35 | 1.04 | 0.015 | 0.01 | 27.9 | Balance |
Wt. %
C Si P S Cr Fe
2.35 1.04 0.015 0.01 27.9 Balance
Mechanical Test of weld Metal
|
pure weld deposit | 1 layer on steel with C = 0.15% | 1 layer on high Mn-steel |
| Typical |
60 | 55 | 52 |
Typical
pure weld deposit 1 layer on steel with C = 0.15% 1 layer on high Mn-steel
60 55 52
Operating Data
|
2.5mm | 3.2mm | 4.0mm | 5.0mm |
| L mm |
350 | 350 | 350 | 350 |
| Amps A |
80-100 | 90-130 | 130-180 | 140-190 |
L mm
2.5mm 3.2mm 4.0mm 5.0mm
350 350 350 350
Amps A
2.5mm 3.2mm 4.0mm 5.0mm
80-100 90-130 130-180 140-190
- Hold stick electrode as vertically as possible, keep a short arc. Preheating is in general not necessary.
On multipass-applications a cushion layer with HF90 is recommended in order to prevent hardening cracks in the weld deposit. Re-dry stick electrodes that have got damp for 2h/300° C.