Weld metal deposit analysis
|
C | Si | Mn | P | S | Ni | Mo |
| Wt. % |
0.12 | 0.40 | 1.75 | 0.01 | 0.01 | 0.5 | 0.36 |
| Typical According to ASME II part C/SFA 5.5 |
0.15 Max | 0.80 Max. | 1.65-2.0 | 0.03 Max. | 0.03 Max. | 0.9 Max | 0.25-0.45 |
Wt. %
C Si Mn P S Ni Mo
0.12 0.40 1.75 0.01 0.01 0.5 0.36
Typical According to ASME II part C/SFA 5.5
C Si Mn P S Ni Mo
0.15 Max 0.80 Max. 1.65-2.0 0.03 Max. 0.03 Max. 0.9 Max 0.25-0.45
Mechanical Test of weld Metal
|
Yield Strength | Tensile Strength | Elongation L0=5d0 | Impact values In J CVN |
|
MPa | MPa | % | -50 oC |
| Tempered at 620 °C/1h |
630 | 720 | 22 | 54 | 53 | 55 |
| Typical According to ASME II part C/SFA 5.5 |
≥ 600 | ≥ 690 | ≥ 16 | ≥ 27 |
Tempered at 620 °C/1h
Yield Strength Tensile Strength Elongation L0=5d0 Impact values In J CVN
MPa MPa % -50 oC
630 720 22 54 53 55
Typical According to ASME II part C/SFA 5.5
Yield Strength Tensile Strength Elongation L0=5d0 Impact values In J CVN
MPa MPa % -50 oC
≥ 600 ≥ 690 ≥ 16 ≥ 27
Operating Data
|
2.5mm | 3.25 mm | 4.0mm | 5.0mm |
| L mm |
350 | 350 | 350 | 350 |
| Amps A |
75 -100 | 110 -140 | 150 -190 | 190 -260 |
L mm
2.5mm 3.25 mm 4.0mm 5.0mm
350 350 350 350
Amps A
2.5mm 3.25 mm 4.0mm 5.0mm
75 -100 110 -140 150 -190 190 -260