It is suitable for claddings on parts subject to highest pressure and shock in combination with |
Description
Material Type Alloy Components
High Iron, Chromium, Manganese and Other elements (Ni).
Weld Deposit Characteristics
It is suitable for claddings on parts subject to highest pressure and shock in combination with abrasion. Surfacing can be made on ferritic steels as well as austenitic hard Mn-steels and joints of hard Mn-steels can be welded. Due to the addition of Cr, increased resistance against friction and corrosion. Very high work hardening and high toughness.
Weld Deposit Properties
Recommended Application
Main application fields are in mines, quarries, cement industry, railways and steel works, where working parts are regenerated, such as breaker jaws, hammer crushers, switches and crossings. Fully austenitic structure.
Standard Sizes
Diameter: 2.5/3.25/4.0/5.0 mm
Packing : 5.0 Kg Packages – 2.0 Kg Vacuum Package
Operating Data
Welding Positions
- All Positions Except Vertical Down
Polarity
- AC & DC (+)
Notes on usage:
Hold the stick electrode vertically. Weld at a low temperature and keep interpass temperature below 250°C. It is recommended to weld short beads and to avoid overheating. Re-drying: 2h/300°C.
We do hereby certify that; the weld metal deposit, has been tested, mechanically and chemically and all results are comply with the requirements of specifications of Elkadesia for engineering industries and the Specification of ASME II part C SFA 5.01 Class C5 and level of tests in J or 5.