high-alloy fully austenitic Cr-Ni-Mo-Cu electrode designed for welding 1.4539/ASTM 904L type steels. It can also be used for welding 1.4404/ASTM 316 components where a ferrite free weld is required, e.g. in cryogenic or non-magnetic applications. The weld metal has a very good impact toughness at low temperatures. To minimize the risk of hot cracking when welding fully austenitic steels, heat input and interpass temperature must be low and there must be as little dilution as possible from the parent metal.


Download Nulled WordPress Themes
Download WordPress Themes Free
Download Nulled WordPress Themes
Download Nulled WordPress Themes
free download udemy course
download redmi firmware
Download Nulled WordPress Themes
online free course

Typical Composition of all-weld Metal

Wt. %

C Si Mn Ni Cr Mo Cu
0.02 0.7 1.21 25.0 20.5 4.8 1.6

Mechanical Properties of all-weld Metal


Yield Strength Tensile Strength Elongation L0=5d0 Impact values In J CVN
MPa MPa % - 40 oC - 196 oC
420 610 34 85 55

Operating Data

L mm

2.5mm 3.25 mm 4.0mm 5.0mm
350 350 350/450 350/450

Amps A

2.5mm 3.25 mm 4.0mm 5.0mm
35-75 55-110 100-150 140-190