KADESIA E 7016-G – ElKADESIA Engineering Industries

Rated 0 out of 5

( 0 customer reviews )

AWS A5.1: E 7016-G

EN 10204 Type 3.1

Description

Basic coated electrode for high-quality welds. Good weldability in all positions except vertical – down. The metal recovery is about 110 % and very low hydrogen content. Weld metal extremely ductile, crack and ageing resistant, thus especially suited for rigid weldments with heavy seam cross sections. CTOD tested at -10 ^oC.

Coating: Lime coated (CaCO3, CaF2, FeMn, FeSi).

Category:Low Hydrogen Groups

Description

Typical Composition of all-weld Metal

	C	Si	Mn	P	S	Ni	Cr	Mo	V
Wt. %	0.06	0.51	1.14	0.01	0.01	0.02	0.04	0.03	0.02
Typical According to ASME II part C/SFA 5.1	0.15 max.	0.75 max.	1.60 max.	0.035 max.	0.035 max.	0.30 max.	0.20 max.	0.30 max.	0.08 max.

Mechanical Test of weld Metal

Heat Treatment	Yield Strength	Tensile Strength	Elongation L0=5d0	Impact values In J CVN
	MPa	MPa	%	-50 ^oC
Untreated	442	540	28	98 / 95 / 96
Average Reference According to ASME II part C/SFA 5.1	≥ 400	≥ 490	≥ 22

Soundness (x-ray): OK
Moisture test: OK
Diffusible hydrogen limit for weld as per ASME II Part C: OK
Deposition efficiency 110 %.

Operating Data

Re – drying: if necessary: 300 – 350 ºC, min. 2 h.

	2.5 mm	3.2 mm	4.0 mm	5.0 mm
L mm	250/350	350/450	350/450	350/450
Amps A	80-110	100-140	130-180	180-230

Welding Positions

All, except vertical down

Polarity

DC (+)

Our Location

Call Center

Email

Social network

Our Products

Typical Composition of all-weld Metal

Mechanical Test of weld Metal

Operating Data

Welding Positions

Polarity

Our Location

Call Center

Email

Social network

Typical Composition of all-weld Metal

Mechanical Test of weld Metal

Operating Data

Welding Positions

Polarity

Related Products

KADESIA IM E7018-1

KADESIA E 6018

KADESIA E 6015

KADESIA E7018-1H4