Typical Composition of all-weld Metal
|
C | Si | Mn | P | S |
| Wt% |
0.08 | 0.4 | 0.5 | 0.01 | 0.01 |
Wt%
C Si Mn P S
0.08 0.4 0.5 0.01 0.01
Mechanical Properties of all-weld Metal
|
Yield Strength 0.2% | Tensile Strength | Elongation L0=5d0 | Impact values In J CVN |
|
MPa | MPa | % | +20 oC | +0 oC | - 20 oC |
| Untreated |
450 | 535 | 26 | 110 | 90 | 50 |
| Typical According to ASME II part C/SFA 5.1 |
≥ 330 | ≥ 430 | (≥ 17 | (≥ 55 | (≥ 47 | (≥ 47 |
Untreated
Yield Strength 0.2% Tensile Strength Elongation L0=5d0 Impact values In J CVN
MPa MPa % +20 oC +0 oC - 20 oC
450 535 26 110 90 50
Typical According to ASME II part C/SFA 5.1
Yield Strength 0.2% Tensile Strength Elongation L0=5d0 Impact values In J CVN
MPa MPa % +20 oC +0 oC - 20 oC
≥ 330 ≥ 430 (≥ 17 (≥ 55 (≥ 47 (≥ 47
Operating Data
|
2.5mm | 3.2mm | 4.0mm | 5.0mm |
| L mm |
350 | 350/450 | 350/450 | 350/450 |
| Amps A |
60-100 | 90-130 | 110-170 | 170-240 |
L mm
2.5mm 3.2mm 4.0mm 5.0mm
350 350/450 350/450 350/450
Amps A
2.5mm 3.2mm 4.0mm 5.0mm
60-100 90-130 110-170 170-240
Base Materials
Steels up to a yield strength of 420 MPa (60ksi) S235JR-S355JR, S235JO-S355JO, P195TR1- P265TR1, P195GH-P265GH, L245NB-L360NB, L245MB-L360MB, L415NB, L415MB, shipbuilding steels: A, B, D ASTM A 106, Gr. A, B; A 283 Gr. A, C; A 285 Gr. A, B, C; A 501, Gr. B; A 573, Gr. 58, 65, 70; A 633, Gr. A, C; A 711 Gr. 1013; API 5 L Gr. B, X42, X52, X60